Synthesis of high voltage (4.9 V) cycling LiNixCoyMn1−x−yO2 cathode materials for lithium rechargeable batteries

Layered mixed oxides LiNi(x)Co(y)Mn(1-x-y)O(2) (0 ≤x, y≤ 0.5) synthesized by a sol-gel method using tartaric acid as a chelating agent, and their structural and electrochemical properties are investigated by thermal analysis, XRD, SEM, FT-IR and XPS studies. The higher composition of Co leads to cation disorder and shrinks the cell volume. Electrochemical behaviour of the synthesized materials is evaluated by Galvanostatic charge/discharge studies using 2016 type coin cells. The cycling studies are carried out in the voltage limits of 2.7 to 4.6, 4.8 and 4.9 V at current rates of C/10 and C/5 respectively. The composition LiNi(0.4)Co(0.1)Mn(0.5)O(2) exhibits an average discharge capacity of 192 mA h g(-1) at the current density of 0.612 mA cm(-2) (C/5) in the voltage range of 2.7-4.9 V as compared to the discharge capacity of 155 and 175 mA h g(-1) in the potential range of 2.7-4.6 and 2.7-4.8 V over the 50 investigated cycles. The effect of higher charge voltage at 4.9 V on the electrochemical performance of LiNi(x)Co(y)Mn(1-x-y)O(2) oxide materials has not previously been reported.