High Temperature Low Friction Behavior of h-BN Coatings against ZrO2

This paper presents high temperature low friction behaviors of the h-BN coatings, which were deposited on high-speed tool steel by radio frequency magnetron sputtering. A tribometer was used to investigate high temperature tribological properties of h-BN coatings against ZrO2 from 500 °C to 800 °C. The surface morphology, mechanical properties and chemical states of the worn surface of the friction pair were characterized and investigated systemically. The experimental results show that h-BN coatings are of significant importance to improve high temperature tribological properties of steel. Moreover, it is found that high temperature super low friction of the friction pairs is successfully achieved due to tribochemistry, which plays a key role in forming the in-situ generated Fe2O3/h-BN composites on the worn surface of h-BN coatings. CoFs of the friction pair are as super low as about 0.02 at 800 °C and around 0.03 at 600 °C at the stable stage. The high temperature super low friction mechanism of the friction pair is discussed in detail. The present study opens a new strategy to achieve high temperature super low friction of the friction system during sliding.