A Review: Laser Welding of Dissimilar Materials (Al/Fe, Al/Ti, Al/Cu)—Methods and Techniques, Microstructure and Properties

Modern structural engineering is impossible without the use of materials and structures with high strength and low specific weight. This work carries out a quantitative and qualitative analysis of articles for 2016-2021 on the topic of welding of dissimilar alloys. It is found that laser welding is most widely used for such metal pairs as Al/Fe, Al/Ti, and Al/Cu. The paper analyzes the influence of the basic techniques, methods, and means of laser welding of Al/Fe, Al/Ti, and Al/Cu on the mechanical properties and thickness of the intermetallic compound (IMC). When welding the lap joint or spike T-joint configuration of Al/Fe, it is preferable to melt the steel, which will be heated or melted, by the laser beam, and through thermal conduction, it will heat the aluminum. When welding the butt-welded joint of Al/Fe, the most preferable is to melt the aluminum by the laser beam (150-160 MPa). When welding the butt-welded joint of Al/Ti, it is possible to obtain the minimum IMC and maximum mechanical properties by offsetting the laser beam to aluminum. Whereas when the laser beam is offset to a titanium alloy, the mechanical properties are 40-50% lower than when the laser beam is offset to an aluminum alloy. When lap welding the Al/Cu joint, under the impact of the laser beam on the aluminum, using defocusing or wobbling (oscillation) of a laser beam, it is possible to increase the contact area of electrical conductivity with the tensile shear strength of 95-128 MPa.